The Influence of Shear Rate on the Kinetics of Formation of Thermoplastic Polyurethane
- سال انتشار: 1383
- محل انتشار: نهمین کنگره ملی مهندسی شیمی ایران
- کد COI اختصاصی: NICEC09_179
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1619
نویسندگان
Department of Chemical Engineering, University of Isfahan, ۸۱۷۴۶-۷۳۴۴۱, Isfahan, Iran
Department of Chemical Engineering, University of Groningen, ۹۷۴۷AG, Groningen, The Netherlands
Department of Chemical Engineering, University of Groningen, ۹۷۴۷AG, Groningen, The Netherlands
چکیده
In this paper the rheokinetics of polyurethane formation and the influence of shear rate on its kinetics have been studied. Two different linear polyurethane systems with 0% and 100% hard segments are examined in a cone and plate rheometer. The isothermal increase of viscosity during polyurethane formation has been measured at different shear rates and different temperatures and is modeled with an exponential function. The molecular weight vs. time curves and the reaction kinetic constants have been obtained for various shear rates and temperatures using gel permeation chromatography (GPC). It was concluded that kinetics of polyurethane formation is enhanced as the shear rate is increased. Phase separation is found to be responsible for irregularities in the viscosity build up due to formation of polyurethane with hard segments at high conversions.کلیدواژه ها
Thermoplastic Polyurethane, kinetics, cone and plate rheometer, shear rate, phase separationمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.