Parametric Investigation of Cathodic Disbondment ofEpoxy Phenolic Coating

  • سال انتشار: 1402
  • محل انتشار: پنجمین کنگره بین المللی مهندسی، تکنولوژی و علوم کاربردی
  • کد COI اختصاصی: GERMANCONF05_136
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 102
دانلود فایل این مقاله

نویسندگان

Hamed Dehghani

Amirkabir University of Technology, Department of Polymer Engineering and ColorTechnology, P.O. Box ۱۵۸۷۵-۴۴۱۳, Tehran, Iran

Mohammadreza Mohammadzadeh Attar

Amirkabir University of Technology, Department of Polymer Engineering and ColorTechnology, P.O. Box ۱۵۸۷۵-۴۴۱۳, Tehran, Iran

Mehran Rostami

Department of Nanomaterials and Nanocoatings, Institute for Color Science and Technology(ICST), P.O. Box ۱۶۷۶۵-۶۵۴, Tehran, Iran

چکیده

Organic coatings are considered to be one of the fundamental methods for corrosion control.However, organic coatings are always are defect due to various reasons, such as incompletesurface preparation, the presence of thermal and mechanical stresses after application, etc.To solve this problem, another protective system called cathodic protection is used inconjunction with organic coatings. Combining these two methods reduces the required currentfor cathodic protection, but on the other hand, it leads to a destructive phenomenon calledcathodic disbondment, which is caused by the creation of an alkaline environment at theinterface between the coating/metal, reducing adhesion and causing the coating disbond fromthe metal surface. In this study, the effects of the parameters of coating thickness, sacrificialanode potential, and filler presence in the coating on the cathodic disbondment of ۱۰۰% solidepoxy phenol novalac coating in the presence of barium sulfate filler in ۳.۵% sodium chlorideelectrolyte were investigated. According to the results, increasing coating thickness,decreasing sacrificial anode potential, and filler presence in the coating reduced cathodicdisbondment

کلیدواژه ها

Cathodic disbondment, Filler, Coating , Epoxy phenolic.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.