Effect of Ni on microstructure and hardness of Al- 15%Mg2Si metal matrix composite
- سال انتشار: 1391
- محل انتشار: دومین کنفرانس بین المللی آلومینیوم
- کد COI اختصاصی: IIAC02_061
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1187
نویسندگان
Department of Material, Faculty of Engineering, Semnan University, Semnan, Iran
Department of Material, Faculty of Engineering, Semnan University, Semnan, Iran
School of Metallurgy and Materials, University of Tehran, North Kargar St, Tehran ۱۱۳۶۵-۴۵۶۳, Iran
چکیده
The excellent properties of Al-Mg2Si composites can be seriously affected by the coarse Mg2Si particles and brittle eutectic matrix. Undesired structure of the composite, specially the presence of large Mg2Si particles in as-cast condition, will lead to undesirable characteristics of the composites. In this work effort was made to study the effect of Ni on microstructure and hardness of Al-15%Mg2Si composite which was produced by an in-situ casting method. Microstructural studies were done by optical and scanning electron microscopy. The results showed that with increasing Ni content, Al-Mg2Si binary eutectic structure gradually evolves into Al-Mg2Si-NiAl3 ternary eutectic. The addition of 0.1–5 wt.% Ni to the composite, also increased its hardness from 101 HB to 136 HB, which is equivalent to 35% enhancement in hardness results.کلیدواژه ها
Al-Mg2Si composite; Ni addition; Microstructure; Mechanical propertiesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.