Simulating Atmospheric Corrosion of Sterling Alloy in Sulphuric Gasses and Effect of Adding Germanium, Using Factsage Software
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_409
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1129
نویسندگان
Amirkabir University of Technology
چکیده
Silver plate specimens with two different compositions have been exposed to the atmospheric gases H2S and SO2 in humidified air under carefully controlled laboratory conditions. Air with H2S or SO2 was passed through a circular tube which contains the specimens. Temperature and relative humidity of test condition was carefully controlled. After exposure, the corrosion product formed on the sample surfaces was analyzed with XRD thin layer(grazing). Tarnishing of specimens was measured by glossmeter. Factsage software used to simulating the corrosion condition and predicting the corrosion product composition. Resultsshow that adding Ge to sterling alloy decreases the corrosion rate and increases the tarnish resistance of specimens. Corrosion products shows difference of chemical reactions were happening during exposure. Adding Ge to sterling alloy decreasecorrosion rate and increase tarnish resitance of specimensکلیدواژه ها
Atmospheric corrosion, Simulating, Silver alloys, XRD low angleمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.