Microstructural evolution of ultrafine-grained austenite fabricated by severe plastic deformation in Fe-Ni-C alloy

  • سال انتشار: 1391
  • محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
  • کد COI اختصاصی: IMES06_356
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1273
دانلود فایل این مقاله

نویسندگان

Hamidreza Jafarian

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST),

Ehsan Borhani

Department of Nano technology, Nano-Materials Science and Engineering group, Semnan University,

چکیده

In this paper, microstructure and mechanical properties of austenite in Fe-24Ni-0.3C alloy subjected to accumulative roll bonding (ARB) process and subsequent annealing were studied. After 6 cycles of ARB process, elongated ultrafine-grained (UFG) austenite with mean grain size of 300 nm was obtained. Annealing treatment of 6-cycle ARB processed austenite at temperatures from 773 to 873 K resulted in formation of partly and fully recrystallized austenites with mean grain sizes between 750 nm to 2.5 μm.

کلیدواژه ها

Ultrafine-grains, Transformation induced plasticity (TRIP), Accumulative roll bonding (ARB), Microstructure

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.