EFFECT OF Ni ON MECHANICAL PROPERTIES OF Al-15%Mg2Si METAL MATRIX COMPOSITE
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_299
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1497
نویسندگان
Department of Material, Faculty of Engineering, Semnan University, Semnan, Iran
School of Metallurgy and Materials, University of Tehran, North Kargar St, Tehran ۱۱۳۶۵-۴۵۶۳,
چکیده
The in-situ Al-Mg2Si composites are good candidate for using in many industrial applications because of the presence of Mg2Si intermetallics. But, the presence of coarse primary Mg2Si particles in the composite matrix leads to poor tensile properties. In current research the effect of Ni on mechanical properties of Al-15%Mg2Si composite has been studied. The results showed that addition of Ni decreases the size of primary Mg2Si particles and also changes the morphology of eutectic Mg2Si from flake-like to rod-like. Adding Ni also made raise in the hardness, Ultimate Tensile Strength (UTS) and elongation values of the compositeکلیدواژه ها
composite, Al-Mg2Si composite; Hardness; UTS; Elongationمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.