EFFECTS OF HOT EXTRUSION ON MICROSTRUCTURE OF Al – 16 WT.% Al4Sr IN-SITU METAL MATRIX COMPOSITE CONTAINING DIFFERENT WEIGHT PERCENTAGES OF Cu
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_101
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1434
نویسندگان
School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, P.O. Box: ۱۴۳۹۵-۷۳۱, Iran
Imam Khomeini International University, Qazvin, Iran
چکیده
The effects of hot extrusion on the microstructure of cast aluminum metal matrix composite (MMC) containing 16 wt.% long and bulky Al4Sr intermetallics with different weight percentages (0.3 wt.% - 5 wt.%) of Cu were studied. Microstructural examinations were assessed by the use of optical microscope (OM), scanning electron microscope (SEM) and X-ray diffractometry (XRD). The results showed that hot extrusion with the ratio of 12:1 at 500 ˚C reduces the size ofAl4Sr particles tremendously. The maximum length of Al4Sr particles changes from 222 μm to 95 μm.Due to the presence of coarse particles and intrinsic brittleness of Cu-rich intermetallics before hot extrusion, reaching to suitable mechanical properties is not optimistic. After hot extrusion with optimum parameters, CuAl2 particles alter from coarse to fine; moreover, the distribution mode of precipitates (Al4Sr particles and Cu-rich intermetallics mainly CuAl2) becomes uniformکلیدواژه ها
Metal matrix composite (MMC); Al4Sr intermetallics; Cu-rich intermetallics; Microstructure; Hot extrusionمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.