Effect of premix solution on mechanical properties and gelation behaviors of Al2O3-ZrO2 Composite
- سال انتشار: 1391
- محل انتشار: اولین همایش بین المللی و ششمین همایش مشترک انجمن مهندسی متالورژی ایران
- کد COI اختصاصی: IMES06_094
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1627
نویسندگان
Department of Metallurgy and Materials Science, Faculty of Engineering, ShahidBahonar University of Kerman
چکیده
In this survey, composite parts of Alumina-zirconia was produced by gel-casting method and the impact of differentparameters such as composition of polymeric materials and sintering temperature on strength and microstructure of the final products is investigated. The results showed that increase in green strength of gel-casting samples obtained by the polymerization rate. Furthermore, increase of Cross-linker in the monomer fixed led to the increase in green strength of the produced parts. Bending strength and relative density measurements of the samples showed the highest bending strength and relative density achieved at sintering temperature of 1500oC.کلیدواژه ها
Gel-casting, Alumina-zirconia composite, Sintering temperature, polymerization rateمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.