The effects of anodizing condition and post treatment on the growth of nickel nanowires using Anodic Aluminum Oxide
- سال انتشار: 1389
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 7، شماره: 3
- کد COI اختصاصی: JR_IJMSEI-7-3_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 155
نویسندگان
Chalmers University of Technology
Iran University of Science and Technology
Advanced Material Research Center, Iran University of Science and Technology,
چکیده
The effects of anodizing condition and post treatment on the growth of nickel nanowires, were investigated. A two-step anodizing process was applied in phosphoric and oxalic acid solution. Nickel electrochemical plating was applied to fill Anodic Aluminum Oxide (AAO) pores. For pore filling enhancement, AAO surfaces were treated by silver predeposition. After electroplating, aluminum and oxide layer of some specimens were removed. The results showed that silver preplating increases the pore filling and as the applied voltage becomes higher, the pores diameter decreases.کلیدواژه ها
anodizing, nanopores, aluminum oxide, depositionاطلاعات بیشتر در مورد COI