Application of TiO2 Coated layer on Polysulfone Sublayer For Thin Film Composite Membranes
- سال انتشار: 1391
- محل انتشار: چهاردهمین کنگره ملی مهندسی شیمی ایران
- کد COI اختصاصی: NICEC14_140
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1334
نویسندگان
Membrane Research Group, Nanotechnology Research Institute, Babol University of Technology
چکیده
In a new approach, thin film composite membranes were fabricated by investigating TiO2 nano-particles which were hidden completely between the polamide thin film and the polysulfone support layer. Scanning electron microscopy and atomic force microscopy were used to study cross section and surface morphological properties of NF membranes. wettability of the surface was obtained from contact angle measuring instrument. Permeability and salt rejection of membranes were tested using dead end filtration cell. Antifouling property of membranes was examined by filtration of pepsin solution as a model foulant and measuring total resistance and flux recovery ratio parameters. Morphological studies showed that the new NF membranes showed acceptable thin film formation (compact and smooth surface). Performance experiments of new antibacterial TFC membranes showed good permeability without scarifying the salt rejection. More resistance to the fouling appeared on the surface of new NFs due to the higher hydrophilicity and smoother surface. Antibacteriality of fabricated membranes was tested by disk diffusion methodکلیدواژه ها
Thin Film Composite Nanofiltration Membrane, TiO2 Nano-particles, Antifouling, Antibacterialمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.