Investigating the properties of silicon carbide and HfB۲ nanocomposite
- سال انتشار: 1401
- محل انتشار: یازدهمین کنفرانس بین المللی مهندسی مواد و متالورژی (iMat۲۰۲۲)
- کد COI اختصاصی: IMES16_139
- زبان مقاله: انگلیسی
- تعداد مشاهده: 326
نویسندگان
Mohammadhossein Rezaei Ghavamabad
Faculty of Materials and Manufacturing Processes, Malek Ashtar University of Technology, Tehran, Iran
Faculty of Materials and Manufacturing Processes, Malek Ashtar University of Technology, Tehran, Iran
Faculty of Materials and Manufacturing Processes, Malek Ashtar University of Technology, Tehran, Iran
چکیده
Carbon parts have found wide applications in high temperature conditions, includingaerospace industries. But unfortunately, carbon parts, despite all the advantages theyhave, are quickly oxidized at a temperature of about ۵۰۰ degrees Celsius. The mainlimitation of using carbon parts at high temperatures is their strong oxidation. One of themost effective and widely used methods for protecting carbon materials is the use ofceramic coatings. As a mineral, silicon carbide has properties such as high thermalstability, high fracture toughness, low thermal expansion coefficient, etc. Therefore, it iswidely used in the manufacture of refractory devices, semiconductors, combustionengines, etc. Oxidation of silicon carbide can be active or passive. Active oxidationreduces the strength of the samples, while passive oxidation leads to the formation of acoherent silicon layer on the silicon carbide surface, thereby improving its performancein several applications. Silicon Carbide Composites As an interesting research topic,several works have been reported on the oxidation behavior of silicon carbide. In thisreview, the use of silicon carbide and SiC/HfB۲ composites are discussed using newlypublished sources.کلیدواژه ها
graphite, HfB۲, oxidation resistance. Silicon carbideمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.