Influence of Multiple Coating and Heat Treatment Cycles on the Performance of Nano-TiO۲ Coating in Protection of ۳۱۶L Stainless Steel against Corrosion under UV Illumination and Dark Conditions
- سال انتشار: 1398
- محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 2
- کد COI اختصاصی: JR_IJMSEI-16-2_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 117
نویسندگان
Dept. Materials Science & Engineering, Iran University of Science and Technology
Dept. Materials Science & Engineering, Iran University of Science and Technology
Dept. Materials Science & Engineering Iran University of Science and Technology
چکیده
In this study nanosized TiO۲coatings on the ۳۱۶L stainless steel substrate were prepared by means of dip-coating technique in which thickness of the coating layer increased byrepeating the coating cycles in two different routes: (I) dipping and drying,respectively, were repeated one, three and five times and finally the dried coated sample was heat treated (single); (II) multiple heat treatment performed after each dipping and drying cycle, respectively.The structural, morphological and optical characterizations of coatings as well as thickness of coatings were systematically studied.The photocatalytic activity of the various TiO۲ coatings was investigated based on the degradation of an aqueous solution of Methyl orange.Moreover, thecorrosion protective properties of coatings were evaluated in both dark and UV illumination conditions based on the obtained polarization curves. The results indicated ۱.۷۵ times improvement in photocatalytic reaction rate constant, a two orders of magnitude decrease in corrosion current density in dark condition and about ۱۴۰ mV electrode potential reduction under UV illumination with optimum coating preparation procedure, repeating the cycle from dipping to heat treatment three times, than the sample prepared with one time coating and heat treatment since this procedure provided not only high thickness and defect-free coating but also transparent one.کلیدواژه ها
Nano-TiO۲ coating, Sol-gel, Stainless steel, Multiple coating and heat treatment cycles, Corrosion protection, Photoelectrochemical cathodic protectionاطلاعات بیشتر در مورد COI