Wear behavior of self-propagating high-temperature synthesized Cu-TiO۲ nanocomposites
- سال انتشار: 1400
- محل انتشار: فصلنامه سنتز و تفجوشی، دوره: 1، شماره: 3
- کد COI اختصاصی: JR_SYNSINT-1-3_001
- زبان مقاله: انگلیسی
- تعداد مشاهده: 274
نویسندگان
School of Metallurgy and Materials Engineering, Iran University of Science & Technology, Narmak, Tehran, Iran
aterials Engineering Department, University of Tabriz, Tabriz, Iran
aterials Engineering Department, University of Tabriz, Tabriz, Iran
School of Metallurgy and Materials Engineering, Iran University of Science & Technology, Narmak, Tehran, Iran
Iran Small Industries and Industrial Parks Organization (ISIPO), Tehran, Iran
Institut fur Metallurgie, TU Clausthal, Clausthal-Zellerfeld, Germany
چکیده
In this paper, the copper-based nanocomposites with TiO۲ nanoparticles were synthesized by the self-propagating high-temperature synthesis (SHS) process. The effect of the different amounts of excess copper, in comparison with the stoichiometric ratio (CuO:Ti ratios of ۱:۱, ۲:۱, and ۳:۱), on the phase formation of achieved samples was studied. A thermodynamical study showed that increasing the excess copper powder reduces the adiabatic temperature, which helps the phase formation. The maximum Brinell hardness (۸۹) was obtained for the sample with the CuO:Ti ratio of ۱:۱. Finally, the wear behavior of the synthesized nanocomposites was evaluated by the pin on disk test, and the variation of friction coefficient and lost weight were measured. The friction coefficient decreased by the formation of phases and distribution of titanium oxide particles during the SHS process in the presence of the stoichiometric ratio of CuO:Ti. Therefore, the wear behavior was improved. The lowest depth of wear trace was measured ۰.۶۸ where the ratio of CuO: Ti was ۱:۱.© ۲۰۲۱ The Authors. Published by Synsint Research Group.کلیدواژه ها
Wear behavior, Synthesis, Thermodynamic, Cu-TiO۲مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.