Effect of Fe2O3 addition on crystallization of SiO2-Na2O-CaO system glasses
- سال انتشار: 1391
- محل انتشار: اولین کنفرانس بین المللی مواد پیشرفته
- کد COI اختصاصی: NAMIC01_050
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2083
نویسندگان
Msc. Student, Iran University of Science and Technology
Associate Professor, School of Metallurgy and Materials Engineering, Iran University of Science and Technology
Professor, School of Metallurgy and Materials Engineering, Iran University of Science and Technology
Bsc. Student, Iran University of Science and Technology
چکیده
Crystallization behavior of soda-lime foam glass composition investigated by addition of iron oxide (Fe2O3) up to 32 %wt using reducing agent such as SiC. Crystallization temperature of Fe-bearing Diopside (Fe0.35Al0.2Mg0.44)Ca0.96(Fe0.08Si0.7Al0.2)2O6.12, Acmite/Aegirine NaFe(SiO3)2 decreased with increasing iron content from 900oC to 850 oC. Magnetite plays key role as an intermediate phase on which pyroxene heterogeneously crystallizes. Presence of SiC also intensifies crystallization without remarkable change in temperature. Samples with 29gr part weight Fe2O3, showed desirable foaming behavior along with crystallizationکلیدواژه ها
مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.