Delamination Wear Mechanism in Gray Cast Irons
- سال انتشار: 1379
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 13، شماره: 1
- کد COI اختصاصی: JR_IJE-13-1_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 153
نویسندگان
Mathematics, Isfahan University of Technology
چکیده
An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of ۱۷۰ cm/min, and variable loads of ۲۰-۲۶۰ N for a duration of ۱۵ min. to ۳ hours. The gray cast iron surfaces worn by a process of plastic deformation at the subsurface, crack nucleation, and crack growth leading to formation of plate like debris and therefore the delamination theory applies. No evidence of adhesion was observed. This could be due to formation of oxides on the wear surface which prevent adhesion. Channel type chromium plating 'picked' up cast iron from the counterbody surfaces by mechanically trapping cast iron debris on and within the cracks. The removal of the plated chromium left a pitted surface on the cast iron.کلیدواژه ها
Wear, Delamination Wear, Gray Cast Iron, Chromium Platingاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.