Rheology of Concentrated Polystyrene Solution
- سال انتشار: 1390
- محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
- کد COI اختصاصی: PPSRC2011_274
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1167
نویسندگان
Amirkabir University of Technology, Mahshahr Campus Mahshahr, Khuzestan, Iran
چکیده
Rheological data are essential for designing and monitoring of commercial polymerization processes, and crucial for the control of polymerization at high conversions in such processes due to excessive rate therein. Previous studies on the rheology of polymer solutions revealed that above swelling volume fraction ϕs, molecular model represented for dilute solutions could not predict the systems properly. Thus in this paper we try to illustrate a useful model for viscoelastic behavior of concentrated polymer solutions. Commercial grade polystyrene (PS) (Solarene G144) and ethyl benzene (EB) was used to make a solution samples with three different weight percentages i.e. 50, 70 and 90wt%. Accordingly, complex viscosity, storage and loss modulus as a function of frequency were measured in short amplitude oscillatory tests. Effect of temperature as effective parameter was discussed laterکلیدواژه ها
Rheology, Concentrated Solution, Temperatureمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.