Mechanical and Barrier Properties of Uniaxially Stretched Multilayer Nylon/Clay Nanocomposite Film
- سال انتشار: 1390
- محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
- کد COI اختصاصی: PPSRC2011_165
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1131
نویسندگان
CREPEC, Chemical Engineering Department,Ecole Polytechnique, C.P. ۶۰۷۹, Succ. Centre ville Montreal, QC, H۳C ۳A۷ Canada
چکیده
Multilayer films consisting of a core layer of nylon 6 sandwiched between two linear low density polyethylene layer were produced using a semi industrial cast film extrusion line. The core layer of the films was produced from neat nylon and nylon/clay nanocomposite resins. The films were consequently uniaxially stretched in machine direction. The effect of stretching on crystalline structure as well as mechanical and permeability properties of the samples were investigated. Orientations of the films for both layers: polyethylene and nylon were assessed by FTIR (Fourier Transform Infrared Spectroscopy) and it was found that clay inclusion hinder orientation of the core nylon layer. Interaction of nylon molecules with clay influences the crystalline transformation for nylon/clay nanocomposite film during the stretching.کلیدواژه ها
Nylon, Nanocomposite, Multilayer, Filmمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.