Recycling of Lead Acid Battery Cases Polypropylene in Combination with Thermal Stabilizers and Virgin Polypropylene
- سال انتشار: 1390
- محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
- کد COI اختصاصی: PPSRC2011_051
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2360
نویسندگان
Department of Chemical Engineering, Polymer group, Isfahan University of Technology,Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Department of Chemical Engineering, Polymer group, Isfahan University of Technology
چکیده
In this study, blends of virgin polypropylene (PP) and recycled PP used in lead-acid battery cases at various weight ratios were prepared by a single screw extruder. Melt flow index (MFI) and carbonyl index were measured for evaluation of the changes in chemical structure of the blends during the extrusion process. Oxidative induction time (OIT), was also tested to determine the thermal resistance of the samples. Mechanical properties of the samples were studied by tensile and charpy impact tests. To stabilize the compounds during the extrusion process, combinations of a phenolic (Primary Antioxidant, P-AO) and phosphite (Secondary Antioxidant, S-AO) thermal stabilizers with a metal deactivator (Calcium Stearate, CaSt) were used. An optimum composition of stabilizers in the 40:60 (virgin: recycled) PP blend was obtained by using the Taguchi method design of experiments (DOE). This optimum combination of stabilizers was 1 wt% P-AO, 0.2 wt% S-AO, and 0.5 wt% CaSt. In addition, DOE results showed that the primary antioxidant has the biggest influence on stabilization of PP during the extrusion process. Measurement of OIT parameter of the samples containing optimum combination of stabilizers proved that the thermal resistance of these samples was better than the virgin PP. Carbonyl index measurements of these blends indicated that a little degradation occurred in the extrusion process. The results of impact tests showed that the stabilized 40:60 (virgin: recycled) PP blend containing the optimum combination of stabilizers has the same impact strength as the virgin PP. The tensile test results showed that the stabilization of PP blends with the optimum combination of antioxidants led to the higher elongation at breaks and yield strength as compared to the sample without stabilizers.کلیدواژه ها
Recycled polypropylene, Thermal stabilizer, Antioxidant, Metal deactivator, Design of experimentsمقالات مرتبط جدید
- سنتز نانو ماده اکسیدگرافن و بررسی تاثیر آن بر روی مقاومت شیمیایی رنگ آلکیدی
- پیش بینی نرخ های تولید چندفازی (نفت، گاز و آب) با استفاده از روش های یادگیری ماشین: مرور بر روش ها و کاربردها
- روشهای کنترل داده محور در مهندسی شیمی
- بررسی جداسازی گاز پروپیلن از پروپان در غشای ۶FDA-durene با استفاده از روش شبیه سازی مولکولی
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.