Cell structure, thermal properties and flammability of extruded non-crosslinked LDPE/ Cloisite 20A nanoclay foams
- سال انتشار: 1390
- محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
- کد COI اختصاصی: PPSRC2011_024
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2153
نویسندگان
Institute of Polymeric Materials, Polymer Engineering Department, Sahand University of Technology, Tabriz, Iran
چکیده
In this study non-crosslinked low density polyethylene (LDPE) foams were produced by single screw extrusion process. In this process, talc (SiO2: 65 wt % and MgO: 35 wt %) and n-butane/n-propane were used as nucleating agent and physical blowing agent respectively, as well as glycerol monostearat(GMS) was used to obtain dimensional stability in LDPE foams. The effects of organophilic Montmorillonite (OMMT) Cloisite 20A nanoclay (with 0.1 wt%, 0.3 wt% and 0.6 wt%) on thermal conductivity, flame retardancy and morphology, of LDPE foams have been examined. To study nanoclay dispersion state in LDPE foam matrix, X-ray diffraction (XRD) method, and to observe the foam cell structure an optical microscope were used. Thermal conductivity was determined by a simple transient probe conductivity meter, and the flame retardancy of the samples was examined by flammability test. The optimum nanoclay content was determined by comparison of the results in nanocomposite and neat LDPE foams.کلیدواژه ها
مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.