The effect of foam processing conditions on the foaming dynamics of MMA-St copolymer
- سال انتشار: 1390
- محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
- کد COI اختصاصی: PPSRC2011_016
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1098
نویسندگان
Institute of Polymeric Materials, Polymer Engineering Department, Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
Institute of Polymeric Materials, Polymer Engineering Department, Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
Institute of Polymeric Materials, Polymer Engineering Department, Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Tabriz, Iran
چکیده
In this work, we synthesized styrene-methyl methacrylate (St-MMA) copolymer particles by suspension polymerization process to study the foaming dynamics via visual batch foaming apparatus. The weight ratio of St-MMA was 70 to 30, respectively. The foaming system consisted of the self-sealing observation cell equipped with two glass windows and a stereo microscope attached with a high speed digital camera as well as pressure and temperature controller. The required pentane pressure was supplied by heating of a small pentane flask. The synthesized copolymer particles impregnated by pentane and then foaming dynamics were recorded after a rapid pressure release. Different foaming conditions, like temperature, impregnation time and impregnation pressure on the expansion ratio of St-MMA copolymer was investigated. It was concluded that impregnation pressure, time and temperature have different effects on the foaming ratio at lower and higher impregnation pressures than 3 barکلیدواژه ها
St-MMA copolymer, Foaming dynamics, n-pentane, Suspension polymerizationمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.