Evolution of Texture and Grain Size during Equal Channel Angular Extrusion of Pure Copper and ۶۰۱۲ Aluminum
- سال انتشار: 1394
- محل انتشار: فصلنامه فرایندهای نوین در ساخت و تولید، دوره: 4، شماره: 4
- کد COI اختصاصی: JR_MPMPJ-4-4_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 245
نویسندگان
Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran
چکیده
Among different SPD techniques, Equal channel Angular Pressing has attracted the most attentions, because of applying large strain to solid bulk materials. In this research, ECAP process up to ۶ passes was carried out on a pure copper and a ۶۰۱۲ Al-Mg-Si alloy with BC route in ECAP dies with Φ=۱۲۰ and Ψ=۲۰ and diameter of ۲۰and ۱۰ millimeter respectively. Moreover, X-ray diffraction (XRD) system was utilized to investigate changes of the crystallite size and texture variations using for calculating texture parameters and comparing the X-ray diffraction patterns of annealed samples and Ecaped samples. Dominant texture of (۱۱۱) in annealed aluminum altered to a mixture plane. Also, dominant texture of annealed copper of (۱۱۱) and (۲۰۰) shifted to another plane. The opposite of copper samples, changes in diameter and length of aluminum specimens had no effect on diffraction pattern of them. The microstructures were evaluated by OM. The results showed that grain size of annealed aluminum after six passes of ECAP decreased by ۷۵%.کلیدواژه ها
Aluminum Alloy ۶۰۱۲, Pure Copper, SPD, Equal Channel Angular Pressing, Textureاطلاعات بیشتر در مورد COI