Structural characteristics and tribological properties of TiAlCr(Si)CN nanocomposite films coated on the SPK ۱.۲۰۸۰ tool steel using PVD technique
- سال انتشار: 1396
- محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 5، شماره: 1
- کد COI اختصاصی: JR_JMATPR-5-1_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 542
نویسندگان
Mohammad Hassan Dadkhah Tehrani
Malek-Ashtar University of Technology ۸۳۱۴۵-۱۱۵, Isfahan, IR Iran.
Malek-Ashtar University of Technology
Islamic Azad University ۸۱۵۹۵-۱۵۸, Isfahan, IR Iran.
Islamic Azad University ۸۱۵۹۵-۱۵۸, Isfahan, IR Iran.
Islamic Azad University ۸۱۵۹۵-۱۵۸, Isfahan, IR Iran.
Mohammad Hossein Dadkhah Tehrani
Malek-Ashtar University of Technology ۸۳۱۴۵-۱۱۵, Isfahan, IR Iran.
چکیده
In the present work, structural characteristics and tribological properties of the Ti-Al-Cr-(Si)-C-N nanocomposite films coated on the SPK ۱.۲۰۸۰ tool steel byPVD technique have been investigated. The PVD coating process was carried out using Ti (Si) Al and CrAl cathodes at ۱۵۰ A current, ۴۰ V bias and (Ar)۰.۱(CH۴)۰.۴۵(N۲)۰.۴۵ gas mixture for ۵۰ min. Evaluations were conducted by OM, FESEM, AFM, XRD, nano and micro-indenters, and pin-on-disk tribometer. The uniform films with an about ۲.۵ μm thickness, and ۱۱.۷ and ۹.۵ nm crystallite size values were respectively formed on the Ti-Al-Cr-C-N and Ti-Al-Cr-(Si)-C-N coated specimens. Surface hardness of the Ti-Al-Cr-C-N and Ti-Al-Cr-Si-C-N-coated samples was respectively obtained ۸.۷ and ۱۰.۸ GPa compared to ۲.۱۶ GPa for the un-coated substrate. Roughness (RMS), reduced modulus (E) and H/E ratio related to the Si-incorporated film were respectively determined ۴.۶ nm, ۴۷۷ GPa and ۰.۰۸۱ than that of the ۹.۷ nm, ۳۶۴ GPa and ۰.۰۷۵ for the Si-emptied film. Tribological properties were significantly enhanced by both the films particular the Si-incorporated kind.کلیدواژه ها
tool steel, Ti-Al-Cr-(Si)-C-N, Microstructure, tribological behaviorاطلاعات بیشتر در مورد COI