Effect of MgF۲ Addition on the Mechanical Properties of Hydroxyapatite Synthesized via Powder Metallurgy
- سال انتشار: 1398
- محل انتشار: فصلنامه کامپوزیت ها و ترکیبات، دوره: 1، شماره: 1
- کد COI اختصاصی: JR_JRCC-1-1_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 167
نویسندگان
Materials Engineering, Saveh Islamic Azad University, Saveh, Iran
Research Institute for Advanced Materials and New Energy, Iran Scientific and Industrial Research Organization, Tehran, Iran
Department of Biomaterials Nanotechnology and Tissue engineering, Isfahan University of Medical Sciences, Isfahan, Iran
Department of Medical Nanotechnology, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences (TUMS), Tehran, Iran
چکیده
Hydroxyapatite, a type of bioceramics, is mainly used as an implant for hard tissues due to its similarity to the structure of hard tissues. The aim of this study is to improve the mechanical properties of hydroxyapatite for biological uses. For this purpose the effect of magnesium fluoride (MgF۲) addition with different weight percentages (۰, ۵, ۷.۵ and ۱۰ wt. %) on the mechanical properties of pure hydroxyapatite sintered at various temperatures (۹۰۰, ۱۰۰۰ and ۱۱۰۰ °C) for ۱ hour was investigated. XRD analysis was performed to study the decomposition of hydroxyapatite and the transformed phases. The density, Vickers microhardness and fracture toughness of the specimens were measured. The SEM analysis was performed to investigate the microstructure of samples. The results showed that the decomposition of hydroxyapatite to tri-calcium phosphate (TCP) decreased with increasing MgF۲. Also, an increment in density and mechanical properties of the specimens were observed with increasing the amount of hydroxyapatite. The fracture toughness of sintered pure hydroxyapatite increased from ۲.۳ to ۱.۳ MPa.m۱/۲. The specimen containing ۱۰ wt. % MgF۲ sintered at ۱۱۰۰ °C showed the best mechanical properties.©۲۰۱۹ jourcc. All rights reserved.کلیدواژه ها
Hydroxyapatite, Magnesium Fluoride (MgF۲), Tri-Calcium Phosphate (TCP), Sinterمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.