Investigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
- سال انتشار: 1399
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 33، شماره: 9
- کد COI اختصاصی: JR_IJE-33-9_009
- زبان مقاله: انگلیسی
- تعداد مشاهده: 298
نویسندگان
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
چکیده
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in ۱, ۳, and ۶ of weight percentage compounds. The vial speed was ۳۵۰ rpm and ball to powder weight ratio kept at ۱۵:۱ under Argon atmosphere, and the time of milling was ۹۰ h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS). Crystallite size, lattice strain, and lattice constant were calculated by Rietveld refinement with Maud software. The results show a decrease in the crystallite size, and an increase in the internal strain and lattice parameter. Furthermore, the lattice parameter grew by increasing the percentage of titanium. Then, the powders compressed by the cold press and annealed at ۶۵۰˚C, and finally, their micro-hardness and electrical resistance were measured. These analyses show that via increasing the proportion of titanium, Cu-۶wt%Ti with ۳۱۲ Vickers had the highest micro-hardness; due to the increasing the work hardening. Moreover, the results of the electrical resistance illustrate through increasing the amount of alloying material, the electrical resistance grew which the highest electrical conductivity was Cu-۱wt%Ti with ۰.۳۶ Ω.کلیدواژه ها
Copper-Titanium alloys, mechanical alloying, Electrical resistance, Mechanical propertiesاطلاعات بیشتر در مورد COI