Microstructure and mechanical properties of Graphite reinforced aluminum matrix composites fabricated by multi-passed friction stir processing (FSP)
- سال انتشار: 1399
- محل انتشار: سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب
- کد COI اختصاصی: INCWI21_021
- زبان مقاله: انگلیسی
- تعداد مشاهده: 324
نویسندگان
M.Sc. Student, Sharif university of Technology, Tehran, Iran; hossein
Professor, Department of Materials Science and Engineering, Sharif University of Technology, Tehran,Iran
چکیده
Friction Stir Processing (FSP) is known as a solid state process with a significant capacity of fabricating fine grained surface composites from Aluminum metal matrix. In this work, we used Graphite particles (20-50 μm) as reinforcing secondary phase in AL1050 matrix, in order to improve mechanical properties throughout this process. Graphite particles preplaced into machined grooves in the middle of the aluminum1050 sheet and multi-passed FSP applied. The microstructure of the composites examined byusing optical microscopy (OM) and scanning electron microscopy (SEM). It identified that Graphite particles were well dispersed in the Aluminum matrix throughout the multipassed FSP. In addition, the average grain size of the stir zone decreased due to dynamic recrystallization during the high temperature severe plastic deformation. Tensile tests and microhardness measurement showed that, with the increase of graphite particles content, the tensile strength and microhardness of the Graphite/AL1050 composites remarkably increased, on the contrary, the elongation decreased due to brittle nature of the graphite particles. The maximum ultimate tensile strength reached up to 193 MPa and the microhardness enhanced to 74.4 (HV) when 3 Wt.% Graphite were added. In addition, the composite became more and more brittle when the weight percent of the Graphite content increased.کلیدواژه ها
Friction Stir Processing, Surface composite, Aluminum alloys, Graphite particlesمقالات مرتبط جدید
- Young’s modulus and Poisson’s ratio of enhanced re_entrant
- Vibrations Analysis of star-shaped auxetic plate using the Differential Quadrature Method
- Uterine and ovarian tissue engineering
- Type -I hot corrosion behavior of Cr -modified slurry alumini de coating superalloy Rene ۸۰
- Synthesis and characterization of temperature-sensitive smart hydrogel of polyethylene glycol
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.