Influences of Blank Holder Force in The Multi-Step Deep Drawing Process of Aluminum Sheets
- سال انتشار: 1399
- محل انتشار: مجله بین المللی طراحی پیشرفته و تکنولوژی ساخت، دوره: 13، شماره: 3
- کد COI اختصاصی: JR_ADMTL-13-3_005
- زبان مقاله: انگلیسی
- تعداد مشاهده: 210
نویسندگان
Department of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, Iran
Department of Mechanical Engineering, Faculty of Enghelab-e Eslami, Tehran Branch, Technical and Vocational University (TVU), Tehran, Iran
Department of Mechanical Engineering, Faculty of Industrial and Mechanical Engineering, Qazvin Branch, Islamic Azad University, Qazvin, Iran
چکیده
In recent decades, the use of aluminium alloys is developed in the automotive industry with regard to the need for lightweight and anti-corrosion components, one of which is AA7075 Al alloy. In this study, the multi-step deep drawing process of AA7075 aluminium sheets under various blank holder forces is investigated through a numerical simulation and is then validated with experimental results. Simulations were conducted by ABAQUS finite element software, and the influences of the blank holder force on the wrinkling height, rupture occurrence and thickness distribution of the sheet were studied. The optimum amount of blank holder force at each drawing step is determined so that the height of wrinkling, and the thinning percentage do not exceed the permissible value. Based on the results, the blank holder force magnitude should be considered descending during the four successive steps to achieve more uniform thickness distribution, and also the wrinkling height could be reduced by increasing the blank holder force in the analysed force range. The optimum amount of blank holder force in the four drawing steps was 28000, 2500, 1500 and 600 N, respectively. In general, the minimum thickness was created in the corner of the punch. The results also showed that an excessive increase in the blank holder force in order to eliminate the wrinkling caused the thinning percentage to increase. Finally, a good accordance between the experimental and numerical results was observed.کلیدواژه ها
Blank Holder Force, Deep drawing, Finite Element Analysis, Thickness Distributionاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.