On the Interlaminar Shear Strength of Basalt Fiber/Epoxy Composite Filled with Nano-ZrO2/Graphene Oxide Nanohybrid

  • سال انتشار: 1398
  • محل انتشار: کنفرانس دو سالانه بین المللی مکانیک جامدات تجربی
  • کد COI اختصاصی: WMECH05_083
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 374
دانلود فایل این مقاله

نویسندگان

D Toorchi

M.Sc. Student Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran

H Khosravi

Assistant Professor Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran

E Tohidlou

Assistant Professor Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran

چکیده

Herein, the effect of nano-ZrO2, graphene oxide (GO) and nano-ZrO2/GO hybrid on the interlaminar shear strength (ILSS) of basalt fiber/epoxy composite was investigated. At the first step, the powders were modified by using an amino-ended silane coupling agent. Multiscale composites containing various amounts of nano-ZrO2 (1, 2 and 3 wt.%), GO (0.1, 0.3 and 0.5 wt.%) or nano-ZrO2/GO hybrid in the matrix were fabricated. The results showed that the specimen with 2 wt.% nano-ZrO2+0.1 wt.% GO had the highest values of ILSS (77% increase with respect to the neat basalt fiber/epoxy composite). The fracture surfaces of the specimens after test were analyzed for better understanding the fracture mechanisms

کلیدواژه ها

Nanocomposites, Graphene, Surface modification, Mechanical testing

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.