Polyester fabric modification through fabrication of nano-copper compounds
سال انتشار: 1398
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 405
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CBGCONF06_039
تاریخ نمایه سازی: 28 بهمن 1398
چکیده مقاله:
This research introduces a new method of polyester fabric surface modification in order to achieve distinctive features. The copper sulfate, sodium hydroxide and cetyl trimethylammonium bromide (CTAB) were used to synthesize copper nanoparticles, and loaded on the polyester fabric surface. The optimal sample was considered by SEM-EDX, FT-IR and XRD devices. SEM images showed copper nanoparticles in shape of nano -plates with 150 to 600 nm in length and thickness of about 30 nm. The best results obtained on the modified fabric processed at boil for 120 min. According to the results of experiments CuO and Cu0 were synthesized on the fabric.
کلیدواژه ها:
نویسندگان
Mohammad Mahdi Jolaei
Department of Textile Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
Majid Montazer
Department of Textile Engineering, Amirkabir University of Technology, Tehran, Iran.
Abo-Saeed Rashidi
Department of Textile Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
Mohammad Bameni Moghadam
Department of Statistics, Allameh Tabataba’i University, Tehran, Iran.