Synthesis and characterization of new eco-friendly water reducible polyester coating for application in automotive paint systems
- سال انتشار: 1398
- محل انتشار: ششمین کنگره بین المللی پوشش های حمل و نقل، ترافیک و ایمنی
- کد COI اختصاصی: ICAPC06_015
- زبان مقاله: انگلیسی
- تعداد مشاهده: 559
نویسندگان
Color and Polymer Research Center, Amirkabir University of Technology, Tehran, Iran
Polymer and Color Engineering Department, Amirkabir University of Technology, Tehran, Iran
Color and Surface Coating Department, Iran Polymer and Petrochemical Institute, Tehran, Iran
Polymer and Color Engineering Department, Amirkabir University of Technology, Tehran, Iran
چکیده
Environmental issues are a major concern, especially in automotive industries. Recently, water-born coatings have high attraction due to strict health regulations related to emission of hazardous organic solvents from solventbased coatings. Polyester resins have been used for automotive coatings in all layers like primer, basecoat andclearcoat as well as interior or exterior parts, such as air cleaner, oil filters, wheels , bumpers and etc. In this research, a water reducible polyester resin was synthesized by polycondensation polymerization process. Fourier Transform Infrared Spectroscopy (FT-IR) was used to characterize the chemical structure of synthesized polyester resin. CARDURA E10 was added into the reaction vessel at 210˚C during 3h until the epoxy group peak was disappear at 908 cm-1 according to Figure 1. Also, the ring opening of the epoxy groups of CARDURA observed OH groups (3444 cm-1). The results confirmed the disappearance of the anhydride peak (1768 cm-1) and appearance of carbonyl group (1728 cm-1) in the produced resin. Figure 2 shows the visual appearance of synthesized polyester resin which is clear, transparent and yellowish viscous liquid. Acid and hydroxyl values of resulted polyester resin were determined by titration method equal to 61.7 and 60.2 respectively. Also, another polyester resin with different glass transition temperature (Tg) was synthesized and optimized regarding to extent of netrulizing groups to reach stable dispersion.کلیدواژه ها
Polyester- Water reducible- Automotive Coatings- FTIR.مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.