Cyclic intercritical annealing of dual phase (DP) steel
- سال انتشار: 1398
- محل انتشار: هشتمین کنفرانس و نمایشگاه بین‌المللی مهندسی مواد و متالورژی و سیزدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران
- کد COI اختصاصی: IMES13_205
- زبان مقاله: انگلیسی
- تعداد مشاهده: 398
نویسندگان
BSc student at university of tehran, school of metallurgy and materials engineering
Professor at university of tehran, school of metallurgy and materials engineering.
چکیده
Cyclic intercritical annealing treatment was applied on the DP steel with the initial quenched and cold rolled martesnitic microstructures. A rapid grain growth was observed during repetition of intercritical annealing cycle for the DP steel originated from the quenched microstructure with adverse effects on the tensile properties. Conversely, decreased size of martensite islands and formation of chain like morphology of martensite around ferrite grains was observed during thermal cycling of the DP steel originated from the cold rolled microstructure with the consequent enhanced work hardening behavior. Accordingly, the combination of cold rolling and cyclic intercritical annealing was recommended in this work to enhance the work hardening behavior and mechanical properties of DP steels.کلیدواژه ها
DP steels; Thermal cycling; Microstructure; Mechanical propertiesاطلاعات بیشتر در مورد COI