Evaluating Corrosion Behavior of Ni Electroplating on Titanium Substrate
- سال انتشار: 1398
- محل انتشار: هشتمین کنفرانس و نمایشگاه بین‌المللی مهندسی مواد و متالورژی و سیزدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران
- کد COI اختصاصی: IMES13_029
- زبان مقاله: انگلیسی
- تعداد مشاهده: 618
نویسندگان
Bachelor Student, Materials Engineering Department, University of Tabriz, Tabriz, Iran
Bachelor Student, Materials Engineering Department, University of Tabriz, Tabriz, Iran
Bachelor Student, Materials Engineering Department, University of Tabriz, Tabriz, Iran
PhD Student, Materials Engineering Department, University of Tabriz, Tabriz, Iran
چکیده
Ni-plating is one of the most common coating process which is applied to almost every engineering material. In this paper, the electroplating of Ni coat on the pure Titanium substrate was applied successfully and the optimum condition was obtained as below: electrolyte pH (3), temperature (55 °C), average density (5 A/dm2) rate. In order to characterize the interface microstructure field emission scanning electron microscopy were carried out. Morphology and surface roughness were studied with Atomic Force Microscopy and corrosion behavior was studied by polarization The results showed an increase in hardness of surface, gradually improved corrosion potential, greater in polarization resistance in comparison with pure titanium.کلیدواژه ها
Ni Electroplating, Titanium, Corrosion Resistance, Surface Roughnessمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.