The optimization of dispersant content in alumina castable containing nano-titania
- سال انتشار: 1397
- محل انتشار: مجله سرامیک های پیشرفته، دوره: 4، شماره: 4
- کد COI اختصاصی: JR_ACERPT-4-4_003
- زبان مقاله: انگلیسی
- تعداد مشاهده: 450
نویسندگان
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Department of Materials Engineering, Naghshe Jahan Institute of Higher Education, Isfahan, Iran
چکیده
In this research, two series of ultra-low cement high alumina refractory castables containing 0 and 0.4 wt.% of nano-titania were prepared using different amounts of polycarbonic acid (DOLAPIX FF 26) as a dispersant. Several characteristics including microstructure, flowability, mechanical strength, bulk density and apparent porosity of the samples were analyzed. The results showed that the optimum amount of the dispersant was 0.13 wt.% and 0.20 wt.% for castable having no nano-titania and the one containing 0.4 wt.% nano-titania, respectively. The strength of castable containing 0.4 wt.% nano-titania dispersed by 0.20 wt.% of DOLAPIX FF 26 was 1.5 times higher than that of castable without nano-titania (dispersed by 0.13 wt.% of DOLAPIX FF 26). This can be explained by the fact that when the optimum amount of dispersant is used, the well-dispersed nano-titania particles act as a catalyst in the cement hydration reactions and will result in higher strength of the refractory castables.کلیدواژه ها
Alumina refractory castable, Ultra-low cement, Dispersant, Nano-TiO2اطلاعات بیشتر در مورد COI