Fracture Resistance and Failure Mode of Endodontically Treated Premolars Restored with Different Adhesive Restorations
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 261
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-4-1_003
تاریخ نمایه سازی: 20 مهر 1398
چکیده مقاله:
Introduction: The restoration of endodontically treated teeth is a topic that has been studied extensively but it is still a challenge for dental practitioners. The aim of this study was to evaluate fracture resistance, fracture patterns and fracture location of endodontically treated human maxillary premolars restored with direct and indirect composite resin and ceramic restoration. Methods: Eighty non-carious maxillary premolars were selected and divided into four groups (n=20). Endodontic treatment and mesio-occluso-distal preparations were carried out in all the groups except for the control group (group I). Subsequently, the prepared teeth were restored as follows: group II: indirect composite restoration; group III: ceramic restoration; group IV: direct composite restoration. The specimens were subjected to compressive axial loading until fracture occurred. The mode of failure was also recorded. Results: Group I had higher fracture resistance (1196.82±241.74) than the other groups (P<0.05) and group IV exhibited significantly higher values (962.10±165.52) compared to groups II (731.21±85.89) and III (758.18±108.10) (P<0.05). The fracture patterns were significantly different between the composite resin groups and the ceramic group (P<0.05). The most prevalent fracture pattern in the groups II and IV was mixed fracture and in the group III, restoration cohesive fracture was the predominant pattern. With regard to fracture location, the direct composite restorations exhibited more fractures below the CEJ compared to the indirect restorations (P<0.05). Conclusions: Use of direct composite restorations resulted in higher resistance against fracture, but their failure modes may be unfavorable
کلیدواژه ها:
نویسندگان
Nasrin Sarabi
Dental Research Center, Department of Operative Dentistry, Faculty of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran
Habib Taji
General Practitioner, Mashhad, Iran
Javad Jalayer
General Practitioner, Mashhad, Iran.
Negin Ghaffari
General Practitioner, Mashhad, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :