Aging effect on hardness, elasticity modulus and natural frequency of 304 stainless steel (304 SS)

سال انتشار: 1398
محل انتشار: بیست و هفتمین کنفرانس سالانه بین المللی انجمن مهندسان مکانیک ایران
کد COI اختصاصی: ISME27_667
زبان مقاله: انگلیسی
تعداد مشاهده: 508

نویسندگان

Department of mechanical engineering, Shahid Beheshti University

چکیده

The hardening behavior, natural frequency and mechanical properties of 304 austenite stainless steel after aging heat treatment were investigated. Carbide phase precipitation nucleates at austenite and becomes more intense with the increase of time and temperature. Carbides cause severe sensitization in specimens aged at 750 °C, 850 °C and 950 °C for 72 hours. With increasing structuralchanges, it was found that the natural frequencies of the five modulus increase significantly. Mechanical properties were evaluated at room temperature for all the heat-treated samples. A reasonable increase in elasticity modulus and hardening was observed after aging. These promising results are the elaboration of a nondestructive new method for estimating the remaining life for components of different generations under long-term overheated operation conditions.

کلیدواژه ها

Aging, 304 Stainless steel, Hardening, Microstructural changes, Natural Frequency

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.