Sol - gel derived hydroxyapatite nanopowders and nanostructure coating
- سال انتشار: 1386
- محل انتشار: دومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS02_106
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1312
نویسندگان
Materials Engineering Department, Isfahan University of Technology
Materials Engineering Department, Isfahan University of Technology
Faculty of Dentistry, Isfahan University of Medical Science
چکیده
This paper reports on a simple sol–gel technique for fabricating pure nanostructure hydroxyapatite powders and coatings. X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to evaluate the product properties. The in vitro test was performed in a stimulated body fluid (SBF) medium. It was found that at calcination temperatures of 600ºC, the dominant phase of the powders and coatings were HA. TEM showed that the obtained powder after calcination at 600 ºC is composed of hydroxyapatite nano particles (20–30 nm). Hydroxyapatite nanopowders ionic dissolution rate was found to be quite higher than conventional hydroxyapatite and closer to biological apatite owing to its nanostructure dimensionsکلیدواژه ها
Hydroxyapatite; Sol gel; Nanostructure; In vitro; Coatingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.