Influence of Erbium Oxide on Sensing Behaviour of Titanium Dioxide Nanocrystalline Thin Film
- سال انتشار: 1386
- محل انتشار: دومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS02_102
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1349
نویسندگان
Department of Materials Science & Engineering
Department of Materials Science & Engineering
Department of Materials Science & Metallurgy
چکیده
Nanostructured and mesoporous TiO2-Er2O3 thin film gas sensors with various TiO2:Er2O3 molar ratios have been prepared by a new straightforward particulate sol-gel route. XRD and TEM analysis of powders revealed that the Er2O3 introduction retarded anatase-to-rutile transformation, crystallisation and crystal growth. Furthermore, the specific surface area (SSA) was enhanced by introducing Er2O3 into TiO2. Thin films produced under optimised conditions showed excellent microstructural properties for gas sensing applications. They exhibited a remarkable response towards low concentrations of CO (25 ppm) and NO2 (0.5 ppm) gases at low operating temperature of 200ºC.کلیدواژه ها
TiO2, Er2O3, Sol-gel, nanocrystalline, gas sensorمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.