Plastic anisotropy of ultrafine grained Aluminium AA1050 produced by accumulative roll bonding (ARB)

سال انتشار: 1397
محل انتشار: اولین همایش بین المللی قوای محرکه نوین (با محوریت خودروهای برقی)
کد COI اختصاصی: MPTCONF01_071
زبان مقاله: انگلیسی
تعداد مشاهده: 418

نویسندگان

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, Iran

چکیده

In this research, the Plastic anisotropy of ultrafine grained Aluminum AA1050 specimens produced through accumulative roll bonding (ARB) process was investigated. The specimens were produced successfully by the ARB process up to 5 cycles with the amount of 50% thickness reduction in each cycle at room temperature without using lubricant. Additionally, mechanical properties and tensile fracture surfaces of ultra-fine grained aluminum ARBed specimens were evaluated by uniaxial tensile tests, micro hardness measurements, and scanning electron microscopy. By increasing the number of the ARB cycles up to the 5th cycle, tensile strength and micro hardness of ultra-fine grained aluminum increased to 293 MPa and 65HV, respectively. The SEM results showed that ductile fracture mode with large dimples occurring in the annealed specimen, changed to shear ductile fracture with elongated sophomoric shear and fine dimples after the ARB process

کلیدواژه ها

ARB process, Aluminum alloys, Mechanical anisotropy, Ultra-fine grained material

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.