Re-crystallization of 7000 aluminum alloy with minor amounts of scandium

سال انتشار: 1397
محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
کد COI اختصاصی: IIAC05_052
زبان مقاله: انگلیسی
تعداد مشاهده: 387

نویسندگان

Department of Materials Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran

چکیده

In the present study, the effect of adding trace amounts of scandium and zirconium elements to the 7075 alloy on the re- crystallization behavior of one aluminium alloy (7000 series) was investigated. For this purpose, two kinds of Al-Zn- Mg-Cu-Sc-Zr alloys with the same amount of Zr and different amount of Sc were prepared. Homogenization durations and temperatures of alloys after alloying were obtained by DSC analysis and optical microstructure observations. The results showed that the optimum homogenization temperatures for Al-Zn-Mg-Cu-0.05Sc and Al-Zn-Mg-Cu-0.1Sc alloys were 500 0C and 490 0C respectively, and the optimum duration for both alloys was 12 hours. After homogenization of alloys, the re-crystallization behavior of the alloys was investigated by Brinell hardness test. Obtained results showed that although the re-crystallization temperature for both alloys was similar, but it was 130 C for alloys with 30% forming, and 120 C for alloys with 50% strain. The alloys peak hardness was obtained to be 146 HB

کلیدواژه ها

Re-crystalyzation, Al-Zn-Mg-Cu-Sc-Zr, 7000 series aluminium

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.