Investigation of Wear Properties of Aluminum Matrix Composites Reinforced with Silica Nano-particles Fabricated by the Stir Casting

  • سال انتشار: 1397
  • محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
  • کد COI اختصاصی: IIAC05_034
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 476
دانلود فایل این مقاله

نویسندگان

Mahdi Molaei

Faculty of Materials Science and Metallurgy, Semnan University, Semnan, P.O. Box: ۰۲۳۳۳۶۵۴۱۱۹, Iran

Mahboobeh Azadi

Faculty of Materials Science and Metallurgy, Semnan University, Semnan, P.O. Box: ۰۲۳۳۳۶۵۴۱۱۹, Iran

Hossein Tavakoli

Faculty of Materials Science and Metallurgy, Semnan University, Semnan, P.O. Box: ۰۲۳۳۳۶۵۴۱۱۹, Iran

چکیده

In this paper, the effect of silica nano-particles as aluminium matrix composite reinforcing agent on microstructural changes and wear properties have been investigated. This composite was fabricated by the stir casting method and the casting temperature was considered as a variable parameter. The scanning electron microscopy (SEM), the optical microscopy (OM), the energy dispersive spectroscopy (EDS), the Vickers hardness test and the pin on disk wear testing were used to study the microstructure evaluation and mechanical properties of various samples. Results showed that the hardness of aluminium matrix increased about 37% by adding 1 weight percent of silica nano-particles. This increase in the hardness value changed by increasing the casting temperature from 750 to 850 °C. Addition of these nano-particles into the aluminium matrix also caused to increase the wear resistance. The highest coefficient of friction value related to the composite with the casting temperature of 800 °C. The wear mechanism was also affected since nano-particles were added to the aluminium matrix. When the casting temperature changed from 750 to 850 °C, the AlNi phase coarsening was also occurred which affected wear properties of the composite

کلیدواژه ها

Aluminium Matrix Composite; Silica Nano-particles; Stir casting; Hardness; Wear

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.