In situ synthesis of Fe-TiC/Al2O3 hybrid nanocomposite via mechanical activation-assisted combustion reaction of ilmenite-Al-C system

  • سال انتشار: 1397
  • محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
  • کد COI اختصاصی: IIAC05_017
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 607
دانلود فایل این مقاله

نویسندگان

Morteza Fallahi

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran ۱۶۸۴۴, Iran

Mohammad Khoshghadam Pireyousefan

Nanotechnology Department, School of New Technologies, Iran University of Science & Technology (IUST), Narmak, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

Sadjad Sabzalian

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran ۱۶۸۴۴, Iran

Mansour Soltanieh

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran ۱۶۸۴۴, Iran

چکیده

In this research, fabrication of Fe-TiC/Al2O3 nanocomposite from ilmenite-Al-C system was studied using mechanically activated powders. The effects of Al/C molar ratio and heat treatment temperature on synthesized products were investigated. The synthesized nanocomposites were characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Field Emission Scanning Electron Microscopy (FE-SEM) and Raman spectroscopy. The results showed that for the system with Al/C:1/2.5 molar ratio and after ball-milling for 6h, the major formed phases were Fe and TiO2 during heat treatment at 990°C for 3h and the mechanical activation was inefficient. However, for the system with Al/C:2/1 molar ratio not only iron was reduced to some extent during ball milling process, but also the combustion reaction was completed and the Fe-TiC/Al2O3 nanocomposite was fabricated after heat treatment at 990ºC for 3h. The TiC and Al2O3 crystallite sizes were calculated to be 23 and 38 nm, respectively

کلیدواژه ها

nanocomposite, mechanical activation, combustion synthesis, ilmenite, aluminium

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.