Microstructure and mechanical properties of Al1050/Al5052/SiC multilayered composite produced via accumulative roll bonding process

  • سال انتشار: 1397
  • محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
  • کد COI اختصاصی: IIAC05_015
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 440
دانلود فایل این مقاله

نویسندگان

M Tayyebi

Department of Materials Engineering, Sahand University of Technology, Tabriz ۵۱۹۷۸-۱۷۱۶۹, Iran

D Rahmatabadi

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

R Hashemi

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

چکیده

In this paper, the Al1050/Al5052/SiC multilayered composite is fabricated via ARB process. The microstructure and mechanical properties are studied by optical microscopy, scanning electron microscopy, microhardness measurements, and uniaxial tensile test. The microstructure images showed that plastic instability occurred for the Al5052 reinforcement at the 1th cycle and then by increasing the accumulation strain the Al5052 changed from the lamellar state to particle form, and at the last ARB cycle, a composite is prepared with an perfectly distribution of Al5052 and SiC reinforcements. At the initial ARB cycles, the thickness of the Al5052 layers decreased sharply and then by increasing the number of ARB cycle decreased due to work hardening of the layers. By increasing the number of ARB cycles, the microhardness of both Al1050 and Al5052 layers were significantly and continously increased. The ultimate tensile strength of Al1050/Al5052/SiC multilayered composite at the initial sandwich up to the 2th cycle increased and then decreased in the 3th and 4th cycles, and finally increased in the last two cycles. The best mechanical properties were achieved in the final cycle and the maximum values of 14% and 326 MPa were obtained for elongation and tensile strength. This strength value is about 3.58 and 1.49 times higher than that of the initial Al1050 and Al5052, respectively. SEM images of the tensile fracture surfaces at the different ARB cycles, showed that by increasing the number of the ARB cycles, the fracture mechanism changed from ductile to shear ductile.

کلیدواژه ها

ARB process, Al1050/Al5052/SiC composite, SiC particles, Microstructure and Mechanical properties

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.