Fracture behavior investigation of Al/Cu/Mg multi-layered composite produced by ARB process

  • سال انتشار: 1397
  • محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
  • کد COI اختصاصی: IIAC05_014
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 478
دانلود فایل این مقاله

نویسندگان

D Rahmatabadi

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

M Tayyebi

Department of Materials Engineering, Sahand University of Technology, Tabriz ۵۱۹۷۸-۱۷۱۶۹, Iran

A Sheikhi

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

R Hashemi

School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran

چکیده

In this paper, for the first time, fracture behavior of multi-layered composite produced by accumulative rollbonding (ARB) process was investigated. At first, Al/Cu/Mg multi-layered composite was prepared by ARB through seven passes, and the microstructure and mechanical properties were evaluated, and then the plane stress fracture toughness of Al/Cu/Mg were studied via R-curved. The results of microstructure investigations indicated that plastic instability occurred for the both Cu and Mg reinforcing at the primary sandwich and uniform distribution was processed. By increasing the number of ARB cycles, the microhardness of the three layers Al, Cu, and Mg and ultimate tensile strength (UTS) were significantly increased, continually, and UTS reaches to the maximum value of 355.5 MPa. Results of fracture test showed that by increasing the number of ARB cycles, the value of fracture toughness is increased, continually and at the third pass reaches to the maximum value of 40.4 MPam1/2 that it is 4.08, 3.45 and 2.76 times higher than Al, Mg and Cu, respectively. Also, the trends of fracture toughness for Al/Cu/MG are in good agreement with the results of the fracture behavior investigation of Al 1050 produced by ARB.

کلیدواژه ها

multi-layered composite, ARB process, fracture behaviour, mechanical properties and microstructure

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.