Effects of the addition of Mg and raw material molar ratio on the titanium aluminide-aluminia composite formation mechanism

سال انتشار: 1397
محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
کد COI اختصاصی: IIAC05_003
زبان مقاله: انگلیسی
تعداد مشاهده: 580

نویسندگان

Department of Material Science and Engineering, Birjand University of Technology, Birjand, P.O. Box ۹۷۱۷۵/۵۶۹, Iran

چکیده

The effects of the molar ratio of raw materials (TiO2 and Al) and the addition of Mg on the titanium aluminide- alumina composite formation mechanism were investigated. To achieve this goal, three molar ratios of 1.5:6.5, 1.5:3.5 and 3:5 of TiO2 :Al, without the presence of Mg for the first step, and with 2 wt% Mg for the second step were used. A Differential thermal analysis was applied to determine the critical temperatures of each ratio. Based on the DTA results, the heat treatment was performed. It was found that with the increase of the aluminum content, reactions accelerate due to the merge of the sub-reactions, and subsequently, it causes the transient phase number to decrease.For the second step of experiments, Mg was added to the previously mentioned molar ratios of TiO2 and Al. Mg reduced the reaction temperatures and accelerated the reaction processes as a result of a low melting point eutectic formation.

کلیدواژه ها

Titanium aluminides; DTA; Molar ratio; Mechanism; Mg.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.