Formation of TiAl3 coating on titanium sheet to improve the titanium oxidation resistance

سال انتشار: 1397
محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
کد COI اختصاصی: IIAC05_002
زبان مقاله: انگلیسی
تعداد مشاهده: 570

نویسندگان

Department of Material Science and Engineering, Birjand University of Technology, Birjand, P.O. Box ۹۷۱۷۵/۵۶۹, Iran

چکیده

In this research, TiAl3 layers with different thicknesses were deposited on a titanium sheet by immersion of titanium in molten aluminum for different times. The oxidation behavior of the coated titanium at 850°C was investigated and the comparison of the results was made with the oxidation behavior of the uncoated titanium sheet. The results showed that the produced TiAl3 layer could protect the titanium substrate against the oxidation if it contains an appropriate quality, otherwise not only it cannot withstand the oxidation, but also it accelerates the oxidation process of the titanium substrate. The protection mechanisms of the layers were probed into, performing the XRD analysis. It was found that the TiAl3 layer morphology affects oxidation mechanism and oxidation products.

کلیدواژه ها

TiAl3; Oxidation; Mechanism; Thermodynamic; Immersion

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.