The Effect of Heat Treatment on the Microstructural and Superelastic Behavior of NiTi Alloy with 58.5 wt. % Ni

  • سال انتشار: 1398
  • محل انتشار: مجله مواد دوستدار محیط، دوره: 3، شماره: 1
  • کد COI اختصاصی: JR_JEFM-3-1_004
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 516
دانلود فایل این مقاله

نویسندگان

M. Paryab

Mining and Metallurgical Engineering Department, Amirkabir University of Technology, Tehran, Iran

چکیده

The effect of aging process on hardness as well as the superelastic behavior of NiTi shape memory alloy with 58.5 wt. % Ni has been investigated in this paper. The aging process has been performed at different temperatures ranging from 400 oC to 800oC and for various exposure times from 30 min to 8 hours. The results showed an increase in hardness in the temperature range from 400 oC to 500 oC and then a decrease occurs. At constant temperature with prolonged aging time a gradual increase of hardness occurs.  SEM observations showed that there is some precipitation in specimens aged from 600 oC to 800 oC. The decrease of hardness can be due to an increase in precipitate size. The superelastisity investigation at 25 and 60 oC showed that the maximum superelastisit results are related to specimens aged at 400 oC. The superelastisity properties of NiTi were discussed in terms of hardness and microstructure.

کلیدواژه ها

Shape Memory Alloy, Nitinol, heat treatment, Superelasticity, Structural Properties

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.