Produce of Biodegradable Porous Mg-Zn Scaffold via Powder Metallurgy and Coated with Nano HAP Synthesized by Electrodeposition Process

سال انتشار: 1396
محل انتشار: مجله مواد دوستدار محیط، دوره: 1، شماره: 1
کد COI اختصاصی: JR_JEFM-1-1_007
زبان مقاله: انگلیسی
تعداد مشاهده: 620

نویسندگان

School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran.

چکیده

Mg is considered promising degradable material for tissue engineering applications because of good biocompatibility, corrosion and mechanical properties. In the present work, biodegradable porous Mg-1 wt% Zn scaffold was produced by powder metallurgical process and then nano hydroxyapatite (HAP) coating with composition of Ca10(PO4)6(OH)2 on the scaffold was synthesized by pulse electrodeposition and alkali treatment processes to increase the corrosion resistance of the substrate. The results showed that the as-deposited coating consists of HAP, CaHPO4.2H2O (DCPD) and Ca8H2(PO4)6.5H2O (OCP) with plate-like and needle-like morphologies and the post-treated coating was composed of needle-like structure of nano HAP developed almost perpendicularly to the substrate .Electrochemical tests indicated that the corrosion current density reduced from2.731×10-3 to 4.98×10-5 A.cm-2 and the corrosion potential of scaffold increased from -1.451 to -1.37 V. This study revealed that electrodeposition of HA coating is a useful approach to improve the corrosion resistance of porous Mg-Zn scaffold in SBF and to develop Mg-based degradable implants.

کلیدواژه ها

biodegradable scaffold, Mg–Zn, HAP coating, Electrodeposition, Corrosion Resistance

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.