The Influence of the Nickel Content on Microstructure and Mechanical Properties of the Al-Mg Weld Metal
- سال انتشار: 1396
- محل انتشار: مجله مواد دوستدار محیط، دوره: 1، شماره: 2
- کد COI اختصاصی: JR_JEFM-1-2_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 312
نویسندگان
Iranian Institute of Welding and Nondestructive Testing (IWNT), Tehran, Iran.
چکیده
In this investigation, the microstructure and mechanical properties of the Al 5058 weld metals have been studied in respect of Nickel content in the range of 0.5 to 4.5 percent. Samples were produced by automatic TIG welding process in Butt weld condition with different wire feeder speed rate of pure nickel filler metal. The optical metallography and EDX analysis result shows that by increasing of the nickel content in the weld metal, the grain size decreased and the volume fraction of the inter-metallic compounds of Nickel rich phase was increased. The mechanical test results show that by increasing of the nickel content in the weld metal, the tensile and yield strength increased, whilst impact energy and elongation decreased.کلیدواژه ها
nickel, Al 5000 Series, Weld Metal, Microstructure, mechanical propertiesاطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.