Study of magnetic and structural and optical properties of Zn doped Fe3O4 nanoparticles synthesized by co-precipitation method for biomedical application

  • سال انتشار: 1393
  • محل انتشار: مجله علوم نانو، دوره: 1، شماره: 4
  • کد COI اختصاصی: JR_NAMJ-1-4_004
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 297
دانلود فایل این مقاله

نویسندگان

Zahra Rezay Marand

Department of physics, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran | Nanoscience Center, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran

Mitra Helmi Rashid Farimani

Department of physics, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran | Nanoscience Center, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran

Nasser Shahtahmasebi

Department of physics, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran | Nanoscience Center, Faculty of Science, Ferdowsi University of Mashhad, Mashhad, Iran

چکیده

Objective(s): This paper describes synthesizing of magnetic nanocomposite with co-precipitation method.   Materials and Methods: Magnetic ZnxFe3-xO4 nanoparticles with 0-14% zinc doping (x=0, 0.025, 0.05, 0.075, 0.1 and 0.125) were successfully synthesized by co-precipitation method. The prepared zinc-doped Fe3O4 nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), vibrating sample magnetometer (VSM) and UV-Vis spectroscopy.   Results: results obtained from X-ray diffraction pattern have revealed the formation of single phase nanoparticles with cubic inverse spinal structures which size varies from 11.13 to 12.81 nm. The prepared nanoparticles have also possessed superparamagnetic properties at room temperature and high level of saturation magnetization with the maximum level of 74.60 emu/g for x=0.075. Ms changing in pure magnetite nanoparticles after impurities addition were explained based on two factors of particles size and exchange interactions . Optical studies results revealed that band gaps in all Zn-doped NPs are higher than pure Fe3O4. As doping percent increases, band gap value decreases from 1.26 eV to 0.43 eV.   Conclusion: These magnetic nanocomposite structures since having superparamagnetic property offer a high potential for biosensing and biomedical application.

کلیدواژه ها

Biomedical application, Fe3O4 nanoparticles, Saturation magnetization, Superparamagnetism, Zn-doping

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.