Synthesis of barium hexaferrite nanoparticles by sol-gel method

  • سال انتشار: 1388
  • محل انتشار: سومین کنفرانس نانوساختارها
  • کد COI اختصاصی: CNS03_352
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 2148
دانلود فایل این مقاله

نویسندگان

E Mohammad Sharifi

Department of Materials engineering, Isfahan University of Technology, ۸۴۱۵۶, Iran

A Ghasemi

Department of Materials engineering, Malek Ashtar University of Technology, ۸۴۱۵۴, Iran,

چکیده

Barium hexaferrite can be used for permanent magnets, magnetic-recording media and microwave applications because of the adequate combination of low cost and good magnetic properties. In this work, barium hexaferrite nanoparticles were prepared by sol-gel method. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) experiments were conducted to evaluate structural properties of the samples. The X-ray diffraction patterns of the dried sol calcined at 1000 oC show the formation of single-phase Barium hexaferrite. Transmission electron microscopy (TEM) micrographs showed nano-sized particles of prepared BaFe12O19 with mean particle size of around 20 nm. Furthermore, the grain size of the prepared BaFe12O19 was about 5 nm. High values of coercivity field and high saturation magnetization are obtained for prepared nanoparticles

کلیدواژه ها

Barium hexaferrite; nanoparticles; Sol-gel method; magnetic properties

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.