Poly(methyl methacrylate)/ acid functionalized silica nanocomposite electrolytes for rechargeable lithium batteries
- سال انتشار: 1388
- محل انتشار: سومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS03_080
- زبان مقاله: انگلیسی
- تعداد مشاهده: 3994
نویسندگان
Materials and Chemistry Department, Maleke Ashtar University of Technology, Tehran, Iran
چکیده
Solid electrolyte based on plasticized poly(methylmethacrylate) and acid functionalized silica were fabricated and evaluated for applicability in secondary lithium batteries. Surface of silica nanoparticles modified using chlorosulfonic acid. Ion conductivity of nanocomposites was improved with increasing filler loading up to 10wt% and then decreased. The maximum conductivity value was about 1.19×10-3 S.cm-1 in comparison with 3.63×10-5 S.cm-1 for pure electrolytes at 25°C. Solid polymeric electrolytes showed higher conductivity at elevated temperatures and reach to 2.91×10-3 S.cm-1 for films composed of 15wt% of functionalized silica at 70°C. It was suggested that improvement of transportation properties could be due to acid-base interaction between sulfone groups of modified silica with salt and polymer. According to the results, plastisized poly(methylmethacrylate) and acid functionalized silica nanocomposite electrolytes, could be considered as high-performance electrolyte for secondary lithium-polymer batteries.کلیدواژه ها
Poly(methylmethacrylate); Acid functionalized silica; Lithium batteriesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.